PHYSICAL AND MECHANICAL PROPERTIES OF NANOREINFORCED PARTICLEBOARD COMPOSITES

Abstract

Novel composite materials having desired performance properties can be developed by nanotechnology. The major objective of this research was to produce nanomaterial-reinforced particleboard composites with enhanced physical and mechanical performance. Urea formaldehyde adhesive used to produce particleboard composites was reinforced with nanoSiO(2), nanoAl(2)O(3), and nanoZnO at loading level of 0%, 1%, and 3%. To evaluate physical properties density, thickness swelling, water absorption, and equilibrium moisture content were determined while modulus of rupture, modulus of elasticity, bonding strength, and screw withdrawal strength tests were carried out to evaluate mechanical properties of the particleboard composites. The results acquired in this work revealed that nanomaterial reinforcement technique significantly affected the physical and mechanical performance properties of the particleboard composites. The findings showed that the modulus of rupture, modulus of elasticity, bonding strength, and screw withdrawal resistance of the composites improved by all the nanomaterials used in this study, except 3% nanoZnO. It was also determined that using 1% nanoSiO(2) or 1% nanoAl(2)O(3) in the composites had the best results in the bonding strength and screw withdrawal resistance. The findings indicate that it is possible to produce novel wood composites by using proper nanomaterial type and loading level.