Shear bond strength and ultrastructural interface analysis of different adhesive systems to Er:YAG laser-prepared dentin

Abstract

The aim of this study was to evaluate the shear bond strength (SBS) of a microhybrid composite resin bonded with three different adhesive systems to Er:YAG laser- (EL) or bur-prepared dentin surfaces and to analyze the quality and ultrastructure of the adhesive-dentin interfaces by scanning electron microscopy (SEM). The specimens prepared for SBS test and SEM analysis were randomly assigned to eight groups (G1-G8): G1, EL (Fidelis PlusIII, Fotona) + Clearfil S3 Bond (C3S); G2, EL + AdperSE Plus (SE); G3, EL + laser etch + Adper Single Bond2 (SB2); G4, EL + acid etch + SB2; G5, EL + SB2 (no etching); G6, bur + acid etch + SB2; G7, bur + S3; G8, bur + SE. Laser was used in very short pulse mode at a setting of 200 mJ/20 Hz for dentin preparation and at 80 mJ/10 Hz for dentin etching. Bond strength test: 3.5 x 2.0 mm cylindrical molds were placed onto adhesives and filled with the composites. After 24 h in distilled water, SBS was tested at a crosshead speed of 0.5 mm/min. SEM analysis: The dentin-adhesive interfaces were evaluated for the ultrastructure of hybrid layer. Data of SBS (MPa) were statistically analyzed by ANOVA and Tukey HSD. ER:YAG laser-prepared dentin has demonstrated significantly more SBS (p 0.05) in SBS have been determined between the total-etch adhesive applied groups with regard to etching types. SEM analysis revealed that hybrid layers obtained in Er:YAG laser-irradiated dentin exhibited more irregular and non-homogeneous pattern than the conventionally prepared dentin. In conclusion, SE Bond demonstrated superior results in Er:YAG laser-ablated dentin compared to bur-prepared dentin.