dc.identifier.citationYuksel B., Hardal G., "Microstructural and Electrical Properties of 0.5 mol% A1203-0.1 mol% B203 doped ZnO Ceramics", Symposium on Characterization of Minerals, Metals, and Materials held during The-Minerals-Metals-and-Materials-Society Annual Meeting and Exhibition (TMS), California, Amerika Birleşik Devletleri, 16 - 20 Şubat 2014, ss.55-61
dc.identifier.othervv_1032021
dc.identifier.otherav_f4b59929-c003-48e8-8c3d-b589e55efa89
dc.identifier.urihttp://hdl.handle.net/20.500.12627/160403
dc.description.abstractZinc oxide exhibits n-type semiconductivity that is caused by the deviations from stoichiometry. The electrical properties of ZnO can be enhanced by doping a trivalent dopant. It is also important to understand the effect of these dopants on the microstructure of ZnO ceramics. The conventional ceramic processing techniques were used to prepare un-doped and the 0.5 moll)/ii A1203-0.1 mol% B203-doped ZnO ceramics. The samples were sintered at 1200-1400 C for 1 and 3 hours. The microstructure of the samples was investigated by using a scanning electron microscope. The hulk density of the sintered samples was calculated from their weight and dimensions. According to the XRD results, the formation of ZnA1204 phase was confirmed in the samples of 0.5 mol% A1203-0.1 mol% B203-doped ZnO whereas the only ZnO phase was observed in the un-doped ZnO samples. The electrical resistance of the samples was measured at the room temperature.
dc.language.isoeng
dc.subjectMühendislik, Bilişim ve Teknoloji (ENG)
dc.subjectMİNERALOJİ
dc.subjectYerbilimleri
dc.subjectFizikokimya
dc.subjectTemel Bilimler
dc.subjectMühendislik ve Teknoloji
dc.subjectMALZEME BİLİMİ, MULTIDISCIPLINARY
dc.subjectTemel Bilimler (SCI)
dc.subjectKimya
dc.subjectKİMYA, FİZİKSEL
dc.subjectMalzeme Bilimi
dc.titleMicrostructural and Electrical Properties of 0.5 mol% A1203-0.1 mol% B203 doped ZnO Ceramics
dc.typeBildiri
dc.contributor.departmentİstanbul Üniversitesi , Mühendislik Fakültesi , Metalurji Ve Malzeme Mühendisliği Bölümü
dc.contributor.firstauthorID143291


Files in this item

FilesSizeFormatView

There are no files associated with this item.

This item appears in the following Collection(s)

Show simple item record