| dc.contributor.author | Ertürk, Selim | |
| dc.contributor.author | Sezer, Rasit | |
| dc.contributor.author | Hızlı, İbrahim Göksel | |
| dc.contributor.author | Bilen, Aysegul | |
| dc.contributor.author | Arslan, Cüneyt | |
| dc.date.accessioned | 2021-03-05T08:33:04Z | |
| dc.date.available | 2021-03-05T08:33:04Z | |
| dc.identifier.citation | Ertürk S., Sezer R., Hızlı İ. G. , Bilen A., Arslan C., "Roasting of Celestite in Laboratory Scale Rotary Furnace", 8th International Symposium on High-Temperature Metallurgical Processing, California, Amerika Birleşik Devletleri, 26 Şubat - 02 Mart 2017, ss.469-476 | |
| dc.identifier.other | av_997473e5-46d5-4151-829d-066b00ed46a2 | |
| dc.identifier.other | vv_1032021 | |
| dc.identifier.uri | http://hdl.handle.net/20.500.12627/103200 | |
| dc.identifier.uri | https://doi.org/10.1007/978-3-319-51340-9_46 | |
| dc.description.abstract | Turkish celestite ore was roasted in a lab scale rotary kiln furnace with metallurgical coke. Coke and celestite were mixed; the product contained 32% coke which is more than the stoichiometric requirement. 100 g of the mixed product was fed to a rotary furnace at 35 g/min. Temperature (1000 and 1100 degrees C), rotation speed (2.5, 5 and 10 rpm) and the slope of the furnace (2, 3 and 5 degrees) were among the investigated parameters. Phase and chemical analyses were carried out by XRD and XRF techniques, respectively. The maximum solubility of the roasted product in water was 48% under the roasting conditions of 1100 degrees C, 2.5 rpm and 2 degrees slope. | |
| dc.language.iso | eng | |
| dc.subject | Mühendislik, Bilişim ve Teknoloji (ENG) | |
| dc.subject | Mühendislik ve Teknoloji | |
| dc.subject | Metalurji ve Malzeme Mühendisliği | |
| dc.subject | MALZEME BİLİMİ, KARAKTERİZASYON VE TEST | |
| dc.subject | Malzeme Bilimi | |
| dc.subject | METALURJİ VE METALURJİ MÜHENDİSLİĞİ | |
| dc.title | Roasting of Celestite in Laboratory Scale Rotary Furnace | |
| dc.type | Bildiri | |
| dc.contributor.department | İstanbul Teknik Üniversitesi , , | |
| dc.contributor.firstauthorID | 150728 | |