Charge-Compensated n-Type Skutterudites

Abstract

Ba+Yb double-filled n-type skutterudites with a modest degree of charge compensation by Fe on the Co lattice have been synthesized and compacted by spark-plasma sintering, and their thermoelectric properties evaluated at temperatures up to 800 K. Although this approach to making n-type skutterudites seems counterintuitive, the presence of Fe leads to a reduction in the thermal conductivity while it preserves a robust Seebeck coefficient. Consequently, a high ZT in excess of 1.3 was achieved at 800 K in these Fe-containing n-type skutterudite compounds.