Effects of Thermal Annealing and Selective Chemical Etching on Structural and Optical Properties of GaAsBi Epilayer with Droplet Systems

Tarih
2019
Yazar
Erucar, Tulin
Fontaine, Chantal
Kara, Kamuran
Arnoult, Alexandre
Donmez, Ömer
Erol, Ayşe
Üst veri
Tüm öğe kaydını göster
Özet
A GaAs1-xBix layer was grown by molecular beam epitaxy (MBE) with a low Bi content (2.3%) on GaAs maintaining the substrate at a non-rotating state and was then annealed at 750 degrees C, 800 degrees C and 850 degrees C. Each sample that was covered with droplets was investigated by using the Atomic Force Microscopy (AFM), Electrostatic Force Microscopy (EFM) and Photoluminescence (PL) techniques. The surface properties of the GaAs1-xBix layer were investigated by AFM and observed to have a droplet system, which was composed of a donut and a tail. The optical quality of the samples was enhanced after thermal annealing up to 800 degrees C, and the maximum PL intensity was obtained at 750 degrees C. AFM images revealed that the shape of the droplet and tail changed with increasing annealing temperature. EFM images revealed a phase separation on the surface droplet system. To explore the nature of the droplets, previously claimed to be made of Ga and/or Bi, and their effect on PL spectrum, a chemical etch procedure was carried out by using diluted solutions of H2SO4 and/or HCl. We showed that droplets may be efficiently removed from the surface, and PL intensity could be improved by using a proper sequence of chemical etching procedures. Furthermore, the presence of two different phases for the droplet-system observed by EFM was also confirmed by the selective etching procedure.
Bağlantı
http://hdl.handle.net/20.500.12627/22931
https://doi.org/10.1166/jnn.2019.16845
Koleksiyonlar
  • Makale [92796]

Creative Commons Lisansı

İstanbul Üniversitesi Akademik Arşiv Sistemi (ilgili içerikte aksi belirtilmediği sürece) Creative Commons Alıntı-GayriTicari-Türetilemez 4.0 Uluslararası Lisansı ile lisanslanmıştır.

DSpace software copyright © 2002-2016  DuraSpace
İletişim | Geri Bildirim
Theme by 
Atmire NV
 

 


Hakkımızda
Açık Erişim PolitikasıVeri Giriş Rehberleriİletişim
sherpa/romeo
Dergi Adı/ISSN || Yayıncı

Exact phrase only All keywords Any

BaşlıkbaşlayaniçerenISSN

Göz at

Tüm DSpaceBölümler & KoleksiyonlarTarihe GöreYazara GöreBaşlığa GöreKonuya GöreTürlere GöreBu KoleksiyonTarihe GöreYazara GöreBaşlığa GöreKonuya GöreTürlere Göre

Hesabım

GirişKayıt

Creative Commons Lisansı

İstanbul Üniversitesi Akademik Arşiv Sistemi (ilgili içerikte aksi belirtilmediği sürece) Creative Commons Alıntı-GayriTicari-Türetilemez 4.0 Uluslararası Lisansı ile lisanslanmıştır.

DSpace software copyright © 2002-2016  DuraSpace
İletişim | Geri Bildirim
Theme by 
Atmire NV